-
- News
- Books
Featured Books
- design007 Magazine
Latest Issues
Current IssueLevel Up Your Design Skills
This month, our contributors discuss the PCB design classes available at IPC APEX EXPO 2024. As they explain, these courses cover everything from the basics of design through avoiding over-constraining high-speed boards, and so much more!
Opportunities and Challenges
In this issue, our expert contributors discuss the many opportunities and challenges in the PCB design community, and what can be done to grow the numbers of PCB designers—and design instructors.
Embedded Design Techniques
Our expert contributors provide the knowledge this month that designers need to be aware of to make intelligent, educated decisions about embedded design. Many design and manufacturing hurdles can trip up designers who are new to this technology.
- Articles
- Columns
Search Console
- Links
- Events
||| MENU - design007 Magazine
Material Witness: Using Scaled Flow Data
September 16, 2015 | Chet GuilesEstimated reading time: 5 minutes
The IPC TM-650 Scaled Flow Test (2.4.38) uses three values to determine pressed thickness and flow of a given resin system: Ho (the theoretical value of a pressed sample assuming no air entrainment and no flow calculated from the weight of the test stackup), Hf (the actual final thickness per ply measured by micrometer after the flow test) and ΔH (the difference between Ho and Hf expressed in mils of thickness change).
Based on work done originally by Bartlett, Bloechele and Mazeika at Bell Labs in New Jersey [1] and discussed in relation to specific grades of epoxy prepreg by Del, Marx and Sallo of Fortin Laminating [2], scaled flow has long been used in the industry for characterizing epoxy prepregs used for manufacturing multilayer PWBs.
The scaled flow test depends on understanding the Integrated Flow Value for a prepreg system, which can be expressed as
Flow ~ C * (P/A) * Integral (1/η) (from time 0 to ∞)
Where: C is a constant for the particular resin system determined empirically
(P/A) is the ratio of pressure (psi) to area (in2)
Integral (1/η) is the integral of 1/viscosity (poise) taken over the melt, flow and cure cycle
The flow at any given moment is inversely proportional to the viscosity, so the integral takes into account the changing viscosity as the resin first melts and then starts to cure. The ΔH value of the scaled flow test is a measure of the integrated flow during the entire test, and as we will see, the flow of prepreg during MLB fabrication can be controlled by taking this ΔH value into consideration.
The basic scaled flow test uses either 10 plies 5.5” x 7” for heavier glass fabrics such as 2113, 2116, etc. or 18-20 plies for lightweight glass fabrics such as 106 and 1080. These stacks are designed to provide approximately equal masses of material regardless of glass style to normalize the test parameters. (A substantially heavier stack would heat up unevenly and more slowly, and a substantially lighter stack would heat up too fast and give doubtful results.)
The stack weights are used to calculate Ho based on the glass weight and density as well as the resin weight and density. The original scaled flow test was based on conventional FR-4 epoxy whose resin density was approximately 1.35. Nominal values of glass weight and density and resin weight and density are used for doing the calculation of Ho based on actual stack weight.
Resin systems whose density is not very near 1.35 do not quite fit into the official IPC test method because all the stack weight data used assumes epoxy resin of a standard 1.35 density. Any resin whose density varies from that value requires a new set of calculated weights for various stack-ups in order to provide precise data. This is especially true of filled systems whose resin density now includes a ceramic component as well as the organic resins themselves and may have densities higher than standard. For example, a filled polyimide resin whose density is 1.41 would appear to be pressing too thin if the Ho was calculated based on epoxy calculations at 1.35; and conversely, a polyimide system whose resin density was 1.30 (because of low or no Bromine content) would seem to be pressing too thick if calculations were performed based on a standard epoxy at density 1.35. I mention this because there is a tendency to use the IPC method as if the table of basis weights is gospel, while in fact it is only valid for resin systems whose density is that of standard FR-4.
Because our primary interest is in final pressed thickness, scaled flow testing provides a useful tool for making first order approximations of this critical value, and also provides a useful value (ΔH) for adjusting pressure to achieve desired levels of flow.
This relationship can be expressed roughly as:
P = k * (1/ ΔH) * A * [√(W)/ √(L)]
Where: k is a constant based on the resin system and units (~1 for conventional polyimide systems)
(1/ ΔH) is the reciprocal of the ΔH value from the scaled flow test
A is the area of the MLB being pressed
[√(W)/ √(L)] is a “shape factor” using the ratio of the square roots of the width and length
An 18 x 12 lamination size with a k of 1.0 gives the following data. As you can see in Figure 1, at ΔH 0.5 the laminating pressure is about 350 psi, which can be adjusted as needed for a particular design, or reduced somewhat if vacuum lamination is used, and so forth. The point is that with a normal range of ΔH = 0.4 to 0.8 you can quickly see how to adjust pressure to compensate for any flow issues. At very low values of ΔH, the pressure requirement to achieve adequate flow will rise rapidly – as might be the case with out of date prepreg, or low-flow prepreg if flow and fill becomes critical.
Figure 1: Graph showing laminating pressure vs ΔH value for polyimide.
The use of scaled flow has another hidden benefit for thickness control. By using a weight standard rather than a traditional resin content test, any variation in the basis weight of the glass fabric is minimized. Because the density of resin is roughly half that of glass, any change in glass weight will require about double that increase to keep resin content “in spec,” which can result in too thick a pressed thickness per ply. Conversely, if the glass basis weight runs low, reducing resin to achieve the “spec percentage” can result in a laminate that will press too thin.
With pressed ply thickness critical to electrical properties such as impedance (Zo) and to overall board thickness, use of a scaled flow standard based on weight and ΔH results in a tighter control of thickness than would otherwise be achieved. Now some might say this is a small difference, and it may well be in most cases, but when you are building 15-25 layer MLBs, with two or more pieces of prepreg between each inner layer detail, tolerance variations can add up quickly.
Arlon is using a scaled flow method internally to control weights and flows for its lamination grade prepregs with the result that in the past year we have made significant improvements in laminate thickness variability. In newer products such as filled laminates and prepregs, scaled flow would be the material specification of choice for calling our thickness and flow.
Hoping that this brief overview will help those of you who have not been using scaled flow for many years to appreciate the benefits this method can confer. With summer 2015 behind us, this is the Material Witness wishing all a Happy Autumn!
Chet Guiles is a consultant for Arlon Electronic Materials.
Suggested Items
Stan Rak: Elevating the Ideas and Insights of IPC's Thought Leaders Program
04/25/2024 | Stanton Rak, SF Rak CompanyAs a member of the IPC Thought Leaders Program (TLP), I am responsible for identifying knowledge-sharing opportunities that can generate ideas and insights that strengthen the IPC community as well as create a sustainable and lasting future for its members. I am delighted to highlight some of my recent contributions as a member of the TLP.
Alternative Manufacturing Inc. Awarded QML Requalification to IPC J-STD-001 and IPC-A-610
04/24/2024 | IPCIPC's Validation Services Program has awarded an IPC J-STD-001 and IPC-A-610 Qualified Manufacturers Listing (QML) requalification to Alternative Manufacturing Inc (AMI).
IPC Design Competition Champion Crowned at IPC APEX EXPO 2024
04/24/2024 | IPCAt IPC APEX EXPO 2024 in Anaheim, California, five competitors squared off to determine who was the best of the best at PCB design.
Big Win for Defense Production Act Budget Allocation in FY24 Budget
04/23/2024 | I-Connect007 Editorial TeamOne year ago, President Biden issued a determination that chips and packaging are critical for national security. Since that time, much work has been done to continue the conversation in Washington, elevating the importance of the entire chips value chain, and including printed circuit boards and substrates, without which chips cannot operate.
Real Time with... IPC APEX EXPO 2024: A Conversation with IPC's CEO: New Venue, Sustainability, and More
04/23/2024 | Real Time with...IPC APEX EXPOBarry Matties hosts Dr. John W. Mitchell, CEO of IPC, on the final day of IPC APEX EXPO 2024. They discuss the new venue in Anaheim and broach a range of topics, from traffic and booth experiences to workforce development, sustainability, and the CHIPS Act. And they offer advice for newcomers as IPC looks forward to an even better show experience next year.